saturationmagnetization相关论文
A systematic study on the influence of Nd3+ sub-stitution on structural,magnetic and electrical properties of cobalt fer......
Role of compositional changes on thermal,magnetic,and mechanical properties of Fe-P-C-based amorphou
This work aimed to tune the comprehensive properties of Fe-P-C-based amorphous system through investigating the role of ......
Polypyrrole coated-silica/Ni-Zn ferrite (PPy/SiO2/Ni-Zn ferrite) composites were synthesized by an in-situ polymerizatio......
The MM substituted[Nd(1-x)MMx]FeB casting strips were prepared with induction melting and strip casting furnace.The satu......
Bulk metallic glasses(BMGs)have attracted great attention due to their unique properties and potential applications [1].......
Photodegradation of reactive blue 19 dye using magnetic nanophotocatalystα-Fe2O3/WO3:A comparison st
The photocatalytic degradation of reactive blue 19(RB19)dye was investigated in a slurry system using ultraviolet(UV)and......
Magnetic properties of nanocrystalline Fe60Cr40 powders prepared by mechanical alloying in vacuum and air were investiga......
FeNi multilayer films were prepared by EB-PVD technique. A modified TG-DSCapparatus was used to measure their Curie temp......
研究了BaNi2-xCoxFe16O27(x=0,0.2,0.25,0.4,0.42,0.5,0.84)六角铁氧体多晶材料的磁特性。结果,取向度大于75%,介电损耗小于5×10^-3,饱和磁化强度为366KA/m几乎不变。磁晶各向异性场为200kA/m≤Ha≤1140kA/m,这类材料可......
FeNi multilayer films were prepared by EB-PVD technique. A modified TG-DSCapparatus was used to measure their Curie temp......